Compressor for turbine and gas turbine

ABSTRACT

A compressor for a gas turbine, comprises a rotor including a plurality of rotor parts, and blades for a plurality of stages implanted in the rotor parts, the rotor part in which the blades for at least two of the stages are implanted is made of a Ni--Cr--Mo--V low alloy steel, and the Ni--Cr--Mo--V low alloy steel has substantially an entire bainite microstructure comprising, in weight percent, C of 0.15-0.40%, Si not more than 0.1%, Mn not more than 0.5%, Ni of 1.5-2.5%, Cr of 0.8-2.5%, Mo of 0.8-2.0%, V of 0.1-0.35% and the balance being substantially Fe.

CROSS REFERENCE TO RELATED APPLICATION

This is a division of Ser. No. 08/373,770, filed Jan. 17, 1995, which is a continuation-in-part of U.S. Ser. No. 08/275,675, filed Jul. 15, 1995, now U.S. Pat. No. 5,428,953, which is a division of U.S. Ser. No. 08/102,739, filed Aug. 6, 1993, now U.S. Pat. No. 5,360,318.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a high-temperature gas turbine, a compressor for the high-temperature gas turbine, a rotor shaft for the compressor and a heat-resistant steel for the rotor shaft.

2. Description of Related Art

In a compressor rotor for a conventional large-size high-temperature gas turbine, disks (seventeen stages) are fixed thereon by bolts, as disclosed in, for example, Publications of Japanese Laid-Open Patent Applications shou 63-171856 and hei 2-101143. The disks from a first stage to a twelfth stage at a rotor air inlet (low temperature) side are made of a 3% Ni--Cr--Mo--V low alloy steel, while the disks from a thirteenth stage to a sixteenth stage at a rotor air outlet (high temperature) side are made of a Cr--Mo--V low alloy steel having a high strength at high-temperature. The disk of a last stage is made of martensitic steel. This divided rotor type compressor suffers from problems that manufacture thereof requires too many hours and a rupture readily occurs.

Mitsubishi Juko Technical Report, Vol. 27, No. 1 (1990-1) describes another gas turbine compressor with a monolithic rotor shaft.

The disk type gas turbine rotors disclosed in Publications of Japanese Laid-Open Patent Applications shou-63-171856 and hei-2-101143 have disadvantages that manufacture thereof requires too many hours, the bolts are loosened due to creep thereof when a temperature of the compressor is high and thus must be re-tightened with troublesome work to avoid vibrations, and replacement of a broken blade is troublesome.

In recent years, there is a tendency for a capacity of gas turbines to increase and thus for the temperature to also increase.

The compressor rotor for a large-size high-temperature gas turbine is rotated at a high speed in a wide temperature range between room temperature and 500° C. Hence, the monolithic rotor must be made of a material whose room temperature tensile strength is ≧85 kg/mm², fracture appearance transition temperature is ≦20° C. and 475° C., 10⁵ h creep rupture strength under 475° C. and 10⁵ hours is ≧30 kg/mm². The aforementioned Mitsubishi Juko Technical Report does not describe a rotor material, and the compressor disclosed therein is operated at a low temperature. As a rotor material used at high temperature, the above-described Ni--Cr--Mo--V steel has a high toughness at a low temperature but a low strength at high temperature, whereas the above-described Cr--Mo--V steel has a high strength high temperature and a low toughness low temperature.

SUMMARY OF THE INVENTION

An object of the present invention is to provide a reliable compressor rotor in which a monolithic rotor shaft made of a material exhibiting a high high-temperature strength and a high low-temperature-toughness is used, a reliable gas turbine used high temperature for increasing operating efficiency, a compressor for the gas turbine, and a low alloy steel which is used in the rotor shaft.

The present invention provides a high-temperature gas turbine which comprises a compressor, and a turbine coupled to the compressor, the turbine being rotated at a high speed by a combustion gas generated in a combustor. The compressor includes a combined type rotor shaft and blades of at least fifteen stages which are implanted in the combined type rotor shaft. A temperature of a compressed gas generated by the compressor reaches 400° C. or thereabove.

The compressor may include a combined type rotor shaft made of a Ni--Cr--Mo--V low alloy steel and blades implanted in the rotor shaft. The Ni--Cr--Mo--V low alloy steel has a 50%-fracture-appearance-transition-temperature of 20° C. or therebelow and a creep-rupture-strength of 30 kg/mm² or thereabove under 475° C. and 10⁵ hours. More preferably, the Ni--Cr--Mo--V alloy steel has a tensile strength not less than 85 kg/mm² at a room temperature, a 0.2% yield strength not less than 72 kg/mm², an elongation percentage not less than 20%, a contraction percentage not less than 65%, an impact strength not less than 5 kg-m/cm², a 50%-fracture-appearance-transition temperature not more than 20° C., a creep-rupture-strength not less than 30 kg/mm² under 10⁵ hours, and a creep-rupture-strength not less than 37 kg/mm² under 450° C. and 10⁵ hours.

The rotor shaft may be made of a Ni--Cr--Mo--V type low alloy steel having substantially all bainite microstructure which comprises, in weight percent, 0.15-0.40% C, 0.1% or less (therebelow) Si, 0.5% or less Mn, 1.5-2.5% Ni, 0.8-2.5% Cr, 0.8-2.0% Mo, 0.1-0.35% V and the balance substantially formed by Fe. The low alloy steel may contain 0.01-0.1% of at least one material selected from a group consisting of Nb and Ta.

The compressor may include a combined type rotor shaft made of a Ni--Cr--Mo--V type low alloy steel and blades implanted in the rotor shaft. In the rotor shaft, a ratio of a maximum diameter (D) of the rotor shaft to a length (L) between a first stage and a last stage of the blades is 0.40 to 0.55.

The compressor may include at least 15 stages of blades which are implanted in a combined type rotor shaft. All of the blades are implanted in a ring-shaped groove provided over an entire peripheral surface of the rotor shaft.

The compressor may include a combined type rotor shaft and at least fifteen stages of blades which are implanted in the combined type rotor shaft. The blade at a first stage and, if necessary, the blade at at least one stage between a second stage and a fifth stage are inserted separately or independently into the shaft in an axial direction of the shaft to be implanted therein while the blades from the second stage to a last stage with excluding the above-mentioned inserted blade therefrom are implanted in a ring-shaped groove provided over an entire peripheral surface of the shaft.

The compressor may include a combined type rotor shaft and blades of at least fifteen stages which are implanted in the rotor shaft. A first stage and, if necessary, the blade at at least one stage between a second stage and a fifth stage are made of a titanium alloy while the blades from the second stage to a last stage excluding the before-mentioned blade made of titanium alloy, are made of martensitic stainless steel.

The present invention further provides a combined cycle power plant which comprises a gas turbine rotated by a firing gas, a heat recovery steam generator for recovering heat of an exhaust gas discharged from the gas turbine to generate steam, and a steam turbine rotated by the steam, the gas turbine and the steam turbine rotating a generator to generate electric power. The gas turbine includes a compressor. Air is compressed by the compressor with a compression ratio of 15-20 and a temperature of the compressed air is 400° C. or thereabove. A temperature of the firing gas at a combustor outlet is 1400° C. or thereabove. A temperature of the exhaust gas is between 550 and 600° C. The steam turbine has a single casing structure which contains a rotor shaft having a high-pressure rotor and a low-pressure rotor. A temperature of the steam is 530° C. or thereabove, thermal efficiency is 46% or thereabove, and/or a specific power is 600 kW/(kg/S) or thereabove.

The gas turbine may include a compressor having blades of fifteen to twenty stages which are implanted in a combined type rotor shaft. Air is compressed by the compressor with a compression ratio of 15-20 and a temperature of the compressed gas is 400° C. or thereabove. The turbine, rotated by the firing gas, has moving blades of 3 stages. A temperature of the firing gas at a combustor outlet is 1400° C. or thereabove. A temperature of the exhaust gas at an inlet of the heat recovery steam generator is between 550 and 600° C. A temperature of the exhaust gas at an outlet of the heat recovery steam generator is 130° C. or there below. The steam turbine has a single casing structure which contains a rotor shaft having a high-pressure rotor and a low-pressure rotor and blades implanted in the rotor shaft. A blade portion of the blade of a last stage has a size of thirty inches or more. A temperature of the steam at a high-pressure inlet of the steam turbine is 530° C. or more while a temperature at a low-temperature outlet thereof is not more than 100° C.

The present invention further provides a compressor for a gas turbine, having blades implanted in a combined type rotor shaft at multi-stages. The rotor shaft is made of a Ni--Cr--Mo--V type low alloy steel having substantially all bainite microstructure and whose composition comprises, in weight percent, 0.15-0.40% C, 0.1% or less Si, 0.5% or less Mn, 1.5-2.5% Ni, 0.8-2.5% Cr, 0.8-2.0% Mo, 0.1-0.35% V and the balance formed substantially by Fe.

The present invention further provides a rotor shaft for a gas turbine compressor, which has substantially all bainite microstructure, and which comprises, in weight percent, 0.15-0.40% C, 0.1% or less Si, 0.5% or less Mn, 1.5-2.5% Ni, 0.8-2.5% Cr, 0.8-2.0% Mo, 0.1-0.35% V and the balance formed substantially by Fe.

The present invention further provides a heat-resistant steel for a gas turbine compressor rotor, which has substantially all bainite microstructure and substantially comprises, in weight percent, 0.15-0.40% C, 0.1% or less Si, 0.5% or less Mn, 1.5-2.5% Ni, 0.8-2.5% Cr, 0.8-2.0% Mo, 0.1-0.35% V and the balance is formed substantially by Fe.

As compared with a conventional disk-type compressor rotor, since the combined type rotor shaft of the compressor according to the present invention does not require bolting, the temperature of the air can be increased to a higher value, for example, to 400° C., preferably, to a value ranging from 450 to 500° C., thus increasing thermal efficiency by 46% or more. Further, since no creep of bolts occurs, maintenance and inspection can be simplified, and imbalance of rotation can be eliminated, as compared with the conventional disk-type rotor. Further, since a heat-resistant steel having a special alloy composition and exhibiting the characteristics described later is used, blades can be implanted in more than fourteen stages, and a ratio (D/L) of the maximum diameter (D) of the shaft to the length (L) between the first stage to the last stage is between 0.4 and 0.55. That is, the structure similar to that of a conventional disk-type rotor can be obtained. A preferable number of blade stages is more than sixteen with a more preferable number being between eighteen and twenty stages. As a result, the compression ratio can be increased to 15 to 20, preferably, to 16 to 18.

The gas turbine compressor having a combined type rotor shaft according to the present invention has neither stacking bolts nor bolt holes, unlike the conventional divided type rotor. Thus, the number of manufacturing and assembly hours can be greatly reduced. Further, stress relaxation and loosening of the stacking bolts can be eliminated, and reliability for rupture can thus be greatly improved.

Furthermore, the combined type rotor does not require the manufacturing and assembly hours which would conventionally be required for smelting, forging and machining for seventeen disks.

The combined rotor shaft according to the present invention is classified into four types: one of which is formed an integral or monolithic unit, one of which includes a high-temperature portion formed integrally on a body of the rotor shaft, and a combination of an intermediate-temperature portion and a low-temperature portion as divided disks, the combination connected to the body by the bolts, one of which has a high-temperature portion and an integral combination of an intermediate-temperature portion and a low-temperature portion, the integral combination connected to the high-temperature portion by the bolts, and one of which has the high-temperature portion, the intermediate-temperature portion and the low-temperature portion connected to each other by the bolts.

The combined type rotor shaft for a large-size high-temperature gas turbine compressor according to the present invention is made of a Ni--Cr--Mo--V low allow steel because this steel has excellent mechanical properties, particularly, improved bearing characteristics. The rotor shaft made of this low alloy steel has the following composition and a tempered bainite microstructure substantially in whole.

The presence of C improves hardenability and assures sufficient strength. The preferred proportion of C ranges 0.15-0.40% with more preferred being 0.20-0.28%, because the presence of C at 0.15% or below does not ensure sufficient hardenability and hence produces soft ferrite structure around the rotor, thus reducing the tensile strength and deteriorating yield point, and because the inclusion of C at 0.40% or above deteriorates toughness.

Si and Mn act as a deoxidizer. If a steel making technology, such as the vacuum C deoxidation method or the electro slug re-melting method, is used, the addition of Si and Mn is not always necessary to obtain a sound rotor. If Si and Mn are added, however, the proportion thereof must be reduced to 0.1% or below and 0.5% or below, respectively, from the viewpoint of prevention of temper embrittlement, with the preferable proportion (weight percentage) of Si and Mn being 0.05% or below and 0.1%-0.3%, respectively, and more preferable proportion of Mn being between 0.15 and 0.25%.

It is preferable for high-Ni-steel as described below that the Mn content is limited to not more than 0.1 weight %, and it is preferable for low-Ni-steel as described below that the Mn content is limited to 0.5-1.0 weight % and the Si content is limited to 0.1-0.5 weight %.

The presence of Ni is essential to improve hardenability and toughness. The preferable proportion of Ni is equal to or more than 1.5% with a more preferable rate being between 1.6% and 2.0%, because less than 1.5% proportion of Ni is not enough to improve toughness and because more than 2.5% proportion of Ni reduces creep rupture strength.

It is preferable for low temperature rotor parts of a gas-flow upstream side to include a Ni content of 3-5 weight %, and it is preferable for medium temperature rotor parts of a gas-flow middle course to include a Ni content of 0.1-0.7 weight %.

The inclusion of Cr improves hardenability and toughness and impairs the necessary resistance against oxidation in the products at high temperatures. The preferable proportion thereof ranges between 1.2% and 2.2% with a more preferable level ranging between 1.8% and 2.2%, because 0.8% or less of Cr does not ensure the above-described effects sufficiently, and because more than 2.50% of Cr reduces creep rupture strength.

The presence of Mo promotes precipitation of fine carbide in the crystal grains during tempering and thus increases high-temperature strength and high-temperature ductility. The addition of Mo is also capable of restricting segregation or precipitation of impurity elements between the grain boundaries during tempering, and thus can prevent temper embrittlement. The preferable proportion thereof is between 1.0% and 1.7%, because less than 0.8% of Mo does not ensure the above-described advantages and because more than 2.0% of Mo makes the above-described advantages of the addition of Mo substantially saturated.

It is preferable for the high-Ni-steel as described above to include a Mo content of 0.2-0.7 weight percent.

The inclusion of V promotes precipitation of fine carbide in the crystal grains during tempering, and thus improves high-temperature strength and ductility. The preferable proportion of V ranges between 0.21% and 0.28%, because less than 0.10% does not ensure the above-described advantages and because more than 0.35% makes the above-described advantages substantially saturated.

It is preferable for the high-Ni-steel as described above to include a V content of 0.05-0.2 weight percent.

In order to prevent deterioration in the toughness, the proportion of unavoidable impurity elements must be reduced to a sufficiently low value. Particularly, reduction in the proportion of Al greatly improves toughness. The upper limit of Al is set to 0.01% from the viewpoint of the provision of toughness, more preferable proportion of Al is 0.005% or less.

In order to increase the toughness of each of the Ni--Cr--Mo--V steels, the addition of at least one element selected from a group consisting of Nb and Ta is effective. The preferable proportion of the at least one element selected from a group consisting of Nb and Ta ranges from 0.015% to 0.045%, because less than 0.01% thereof is not enough to obtain a sufficiently improved toughness and because more than 0.1% reduces toughness and high-temperature strength.

The addition of not more than 0.4% of at least one, rare earth element or metal, 0.4% or less, Ca 0.1% or less, Mg 0.1% or below Zr, 0.1% or less Ca and 0.1% or less W further increases the strength demanded in the products.

The method of manufacturing the rotor for the large-size high-temperature gas turbine compressor according to the present invention will now be described.

After hot forging and diffusion annealing have been performed on an ingot, refining heat treatment is conducted on the ingot. Quenching in the refining heat treatment is performed first by heating the ingot to an austenitizing temperature ranging from 800 to 1000° C. and then by quenching the ingot by air-blast quenching, water spraying or liquid (water or oil). Next, tempering is conducted by heating the ingot to a temperature ranging from 550 to 700° C. In order to obtain high tensile strength and high creep rupture strength, the austenitizing temperature must be 800° C. or above. Heating to a temperature of 1000° C. or above increases the grain size, and thus reduces toughness. Tempering at 550° C. or below does not ensure high toughness, while tempering at 700° C. or above reduces tensile strength and creep rupture strength.

In order to manufacture a more highly reliable rotor for a large-size high-temperature gas turbine compressor, heating for hardening may be performed in the refining heat treatment at the rotor air inlet side with a relatively low temperature, for example, not more than 350° C., and at the rotor air outlet side with a relatively high temperature, for example, not less than 450° C. The desirable hardening heating temperature at the rotor air inlet (low-temperature) side is from 850 to 925° C. from the viewpoint of reduction in the grain size and increase in the toughness, while the desirable hardening heating temperature at the rotor air outlet (high-temperature) side is from 925 to 975° C. from the viewpoint of provision of a high creep rupture strength. After hardening, tempering is conducted at a temperature ranging from 550 to 700°. To repeat tempering twice is desirable from the viewpoint of decomposition of residual austenite and increase in the toughness. Preferably, a heating temperature of a first tempering is 560-620° C., and that of a subsequent second tempering is higher than that of the first tempering, for example, 600-670° C. A difference in heating temperature between the first and second tempering is preferably 10-20° C. at an air inlet side and 40-60° C. at an air outlet side. The repeat in tempering causes the increases in both tensile strength and impact strength.

In order to manufacture a more reliable rotor for a large-size high-temperature gas turbine compressor, the portion of the ingot at the rotor air inlet (low-temperature) side may be made of a steel having a high toughness, whereas, the portion of the ingot at the rotor air outlet (high-temperature) side may be made from a steel having a high high-temperature strength, and the ingot is formed through the electro slug re-melting method. The ingot is subjected to hot forging and diffusion annealing, and then hardening and tempering.

Next, the rotor and blades for the large-size high-temperature gas turbine compressor according to the present invention and a cooling air introduction hole for a gas turbine disk will be described below.

In the rotor for the large-size high-temperature gas turbine compressor according to the present invention, a cooling air introducing hole must be provided to cool the gas turbine disks and turbine blades by compressed air. This cooling air introducing hole may be provided in a flange portion provided in the rotor. The cooling air introducing hole may be provided between the blades of the last stage and the blades of the second last stage beyond the last stage by dividing the rotor into two parts.

In order to make the gas turbine compressor highly reliable, the rotor blades of long blade length between the first stage and the fifth stage are made of a titanium alloy having a high specific strength, while the rotor blades from the sixth stage to the last stage are made of a 12Cr-type alloy steel.

The blades of the rotor for the large-size high-temperature gas turbine compressor may be shaped such that a hook length (L) is not more than a half of the pitch (P) of the blades.

The compressor rotor shaft may also be made of a tempered-substantially-in-whole martensitic steel whose composition comprises, in weight percent, 0.05-0.2%, more preferably 0.07-0.15% C, 0.1% or less Si or no Si added, 0.4% or less, more preferably 0.1-0.25% Mn, 2-3%, more preferably 2.3-2.7% Ni, 8-13%, more preferably 11-12.5% Cr, 1.5-3%, more preferably 1.8-2.5% Mo, 0.1-0.3%, more preferably 0.15-0.25% V, 0.02-0.2%, more preferably 0.04-0.08% Ta, 0.02-0.2%, more preferably 0.04-0.08% Nb, 0.03-0.1%, more preferably 0.04-0.08% N and the balance substantially of Fe. This martensitic steel may comprises at least one element selected from a group consisting of 0.5% or less Co, 0.5% or less W, 0.01% or less B, 0.1% or less Al, 0.3% or less Ti, 0.1% or less Zr, 0.1% or less Hf, 0.01% or less Ca, 0.01% or less Mg, 0.01% or less Y and 0.01% or less rare earth element or metal. Although such materials have high high-temperature strength and toughness and can thus be used as rotor shaft materials sufficiently, they have low wear characteristics. Hence an additional steel having bainite microstructure with 0.1-0.3% C, 1% or less Si, 2% or less Mn and 0.5-3% Cr, or another additional steel with 1% or less Mo and 0.3% or less V in addition to the composition of the before-mentioned additional steel may be applied to a bearing journal portion of the rotor shaft with a sleeve or multi-layers shape thereon. The multi-layers may be formed through a plurality of cladding steps by welding.

To form the compressor blades, 12% Cr martensitic steel and titanium alloy are usable. The martensitic steel is used to form the moving blades and the stationary blades except for those made of titanium alloy. The martensitic steel is malleable, whose composition comprises 0.1-0.2% C, 0.3% or less Si, 1% or less Mn, 9-13% Cr, 0.5-2% Mo, 0.05-0.2% V and the balance substantially of Fe. Titanium alloy is used to form the blade of the first stage and/or at least one of the blades from the second to fifth stages when necessary. The composition of titanium alloy comprises 0.05% or less C, 3-6% V, 5-8% of Al, 1% or less Fe, and the balance substantially of Ti. Particularly, a blade whose distal end is wider than the implanted portion is desirable because it improves a compression efficiency. The blade made of titanium alloy may be constructed such that the distal end thereof is narrower than the implanted portion thereof or such that the distal end thereof is wider than the implanted portion thereof. The latter structure is used for the blades of the first, second and third stages, and is desirable from the viewpoint of efficiency.

In addition to the compressor rotor shaft, at least one of components including a distant piece, a turbine spacer, a turbine stacking bolt, a compressor stacking bolt and compressor disks of the last stage may be made of a heat-resistant steel having a tempered-substantially-in-whole martensitic structure whose composition comprises, in weight percent, 0.05-0.2% C, 0.5 or less Si, 1% or less Mn, 8-13% Cr, 3% or less Ni, 1.5-3% Mo, 0.05-0.3% V, 0.02-0.2% Nb, 0.02-0.1% N and the balance substantially of Fe. The use of such a heat-resistant steel for all those components ensures a high gas temperature, and improves heat efficiency. Particularly, a highly safe gas turbine exhibiting high embrittlement resistance can be obtained when at least one of the above-mentioned components is made of a heat-resistant steel having a tempered-substantially-in-whole martensitic structure, comprising, in weight percent, 0.05-0.2% C, 0.5% or less Si, 0.6 or less Mn, 8-13% Cr, 2-3% Ni, 1.5-3% Mo, 0.05-0.3% V, 0.02-0.2% Nb, 0.02-0.1% N and the balance substantially of Fe, and having (Mn/Ni) ratio of 0.11 or less, more preferably 0.04-0.10.

A martensitic steel having creep rupture strength of 40 kg/mm² or thereabove under 450° C. for 10⁵ hours and V notch Charpy impact value at 20° C. of 5 kg-m/cm² or thereabove is used as the material for the above-described components. Preferably, a martensitic steel has creep rupture strength of 50 kg/mm² or above under 450° C. for 10⁵ hours, a V notch Charpy impact value thereof at 20° C. obtained after being heated for 10⁵ hours at 500° C. is not less than 5 kg-m/cm².

The above martensitic steel may contain at least one of 1% or less W, 0.5% or less Co, 0.5% or less Cu, 0.01% or less B, 0.5% or less Ti, 0.3% or less Al, 0.1% or less Zr, 0.1% or less Hf, 0.01% or less Ca, 0.01% or less Mg, 0.01% or less Y and 0.01% or less are earth element or metal.

Regarding the diaphragm for fixing turbine nozzles, a portion thereof corresponding to the turbine nozzle of the first stage is made of a material whose composition comprises, in weight percent, 0.05% or less C, 1% or less Si, 2% or less Mn, 16-22% Cr, 8-15% Ni and the balance substantially of Fe, while another portion thereof corresponding to the turbine nozzles of other stages is made of a high C and high Ni type casting steel.

The turbine blade is made of a cast alloy whose composition comprises, in weight percent, 0.07-0.25% C, 1% or less Si, 1% or less Mn, 12-20% Cr, 5-15% Co, 1.0-5.0% Mo, 1.0-5.0% W, 0.005-0.03% B, 2.0-7.0% Ti, 3.0-7.0% Al, at least one of 1.5% or less Nb, 0.01-0.5% Zr, 0.01-0.5% Hf and 0.01-0.5% V, and the balance substantially of Ni, and in which γ' phase and γ" phase are precipitated in the austenitic phase base. For an improved turbine blade used at a more higher temperature, a single crystal alloy in which 5% or less Re is further added to the above-mentioned components, a dispersed alloy in which Y₂ O₃ grains of 0.1 or less μm diameter are uniformly dispersed by 1 or less weight percent, or a unidirectionally solidified alloy is used.

Ni base super alloy, which will be described in detail later, is used to form the gas turbine nozzle at at least a first stage thereof. It may be used to form the gas turbine nozzles at all the stages thereof. The gas turbine nozzle may be made, at the stages other than the first stage, of a cast alloy whose composition comprises, in weight percent, 0.20-0.60% C, 2% or less Si, 2% or less Mn, 25-35% Cr, 5-15% Ni, 3-10% W, 0.003-0.03% B and the balance substantially of Co. The cast alloy may comprise in addition to the aforementioned components, at least one of 0.1-0.3% Ti, 0.1-0.5% Nb and 0.1-0.3% Zr, and include eutectic carbide and secondary carbide in the austenitic phase base. To obtain such alloys, aging treatment is performed after solution heat treatment, and then the aforementioned precipitates are formed to reinforce the alloy.

The gas turbine nozzle at the first stage may be made of Ni base super alloy which has 900° C., 14 kg/mm² rupture strength of 300 h or above and a crack generation resistance of 600 times or above at 900° C. and 350° C. and which can be welded at a preheating temperature of 400° C. or above, has a single blade portion and side walls formed at respective sides of the blade portion, and disposed in a ring-like shape on the outer periphery of the rotatable blade. The Ni base super alloy for the gas turbine nozzle at the first stage may include, in weight percent, 0.05-0.20% C, 15-25% Co, 15-25% Cr, 1.0-3.0% Al, 1.0-3.0% Ti, 1.0-3.0% Nb, 5-10% W and 55% or more Ni, and a total weight percent of (Al+Ti) and the weight percent of W may be within an area defined by lines connecting sequentially points represented by A (Al+Ti 2.5%, w 10%), B (Al+Ti 3%, W 10%), C (Al+Ti 5%, W 7.5%), D (Al+Ti 5%, W 5%), E (Al+Ti 3.5%, W 5%) and F (Al+Ti 2.5%, W 7.5%).

A Ni base alloy having 900° C., 14 kg/mm2 rupture time of 300 h or above is used for the turbine nozzle, and has a preheating temperature which ensures that no crack is generated in a bead having a length of 80 mm and a width of 8 mm and formed by one pass TIG welding at 400° C. or below.

In the gas turbine according to the present invention, the length between the side walls formed at the respective sides of the blade portion of the nozzle is 70 mm or above, and a length from the fire gas inlet side to the fire gas outlet side is 100 mm or above.

Furthermore, in order to prevent corrosion of the turbine blade due to a high-temperature firing gas, Al, Cr or (Al+Cr) diffusion coating may be applied thereto with a coating thickness of 30-150 μm. The coating is preferably performed on a portion of turbine blade exposed to the firing gas. Such the a diffusion coating may be replaced by a combination of a vapor or plasma spraying of Ni or Fe alloy containing 10-30% Cr, 5-10% Al and 1% or less Y, and another subsequent vapor or plasma spraying of stabilizing ZrO₂ to form a heat insulating layer thereof on the Ni or Fe alloy.

The plurality of combustors are provided around the turbine. The combustor has a double structure of an outer cylinder and an inner cylinder. The inner cylinder is formed by welding a plastically workable material having a thickness of 2 to 5 mm and comprising, in weight percent, 0.05-0.2 C, 2% or less Si, 2% or less Mn, 20-25% Cr, 0.5-5% Co, 5-15% Mo, 10-30% Fe, 5% or less W, 0.02% or less B and the balance substantially of Ni. A crescent-shaped louver hole is provided to supply air over the entire periphery of the cylinder. A heat solution treated material having a substantially entire austenitic structure is used. A transition piece for choking the firing gas is provided beyond the combustor. The above-described material is used to form the transition piece.

The steam turbine according to the present invention includes a combined type or monolithic rotor shaft in which multi stages of blades are implanted from the high-pressure side to the low-pressure side, and a casing which covers the rotor. The combined-type rotor shaft is made of a heat-resistant low alloy steel of Ni--Cr--Mo--V type having bainite microstructure. The rotor shaft is formed as a single shaft which extends from the high-pressure side at which steam of 538° C. or 566° C. is introduced to the blade of the first stage to the low-pressure side at which steam of 46° C. or below is exhausted from the blade of the last stage.

The rotor shaft may be made of a heat-resistant low alloy steel of Ni--Cr--Mo--V type having bainite microstructure. The rotor shaft is formed as a single or monolithic shaft which extends from the high-pressure side at which steam of 530° C. is introduced to the blade of the first stage to the low-pressure side at which steam of 100° C. or below is exhausted from the blade of the last stage. The blade of the last stage has a length of 33.5 or 40 inches. The blades from the first stage to another stage having a blade length of 33.5 inches are made of martensitic steel containing 10-13% Cr. The blade having a length of forty inches is made of a Ti base alloy.

The steam turbine according to the present invention may be of a single flow non-reheating type whose steam temperature is 530° C. or above, in which steam of 100° C. is discharged from the low-pressure side and in which steam flows in one direction from the high-pressure side to the low-pressure side, or of a reheating type in which the steam which is heated to the same temperature as that of the high-pressure side is caused to flow into the intermediate pressure side. The steam turbine may have preferably moving blades of ten stages or more. The desirable length of the blade portion of the last stage is preferably thirty inches or above.

The compressor may have another divided-type rotor including a plurality of rotor parts and blades of a plurality of stages e.g., twelve stages, and the blades for at least two of the stages are implanted in one of the rotor parts. For example, the blades for respective pairs of stages in the first to at least sixth stages can be implanted in each of respective ones of the rotor parts. The rotor parts may be made of a Ni--Cr--Mo--V low alloy steel, a 50% fracture appearance transition temperature of the Ni--Cr--Mo--V low alloy steel is not more than 20° C., and 10⁵ hours creep rupture strength under 450° C. is not less than 30 kg/mm². The Ni--Cr--Mo--V low alloy steel has substantially an entire bainite microstructure comprising, in weight percent, C of 0.15-0.40%, Si not more than 0.1%, Mn not more than 0.5%, Ni of 1.5-2.5%, Cr of 0.8-2.5%, Mo of 0.8-2.0%, V of 0.1-0.35% and the balance being substantially Fe. The Ni--Cr--Mo--V low alloy steel may comprise, in weight percent, at least one of Nb and Ta of 0.01-0.1%.

The blades for two or three stages in the first to at least sixth stages (numbered from an upstream side of the air flow toward a downstream side thereof) may be implanted in at least one of the rotor parts. Diameters of the rotor parts in which the blades for the first to at least sixth stages are implanted may be substantially equal to each other, a ratio of an axial length of the rotor between the first stage and the last stage to a maximum diameter of the rotor parts is 3.0-4.0 to 1, and a ratio of the axial length of the rotor between the first stage and the last stage to a minimum diameter of the rotor parts is 3.7-4.7 to 1. The rotor may include at least six rotor parts, and blades for at least fifteen stages implanted in the rotor parts, the blades for two stages in the first to eighth stages are implanted in each four of the rotor parts, and the blades for at least three stages in the ninth to the last stages are implanted in each of the other rotor parts. The blades for the first to at least eighth stages other than the last stage may be implanted in the rotor parts by being inserted into the rotor parts in an axial direction of the rotor, and at least one of the other rotor parts in which the blades for at least three stages of the other stages may be implanted has a ring-shaped circumferential groove for receiving the blades.

The rotor may include at least three rotor parts, and blades for at least fifteen stages implanted in the rotor parts, the blades for the first stage and at least one stage of the second to fifth stages may be made of a Ti alloy, and the blades for the second to the last stages other than the blades made of the Ti alloy may be made of a martensite stainless steel.

In a combined cycle power plant, the rotor may include at least three rotor parts and blades, the blades for at least two stages are implanted in each of the rotor parts, a compression ratio of the air by the compressor is 15 to 20, a temperature of the compressed air is not less than 400° C., a temperature of the combustion gas at a combustor outlet is not less than 1400° C., a temperature of the exhausted combustion gas is 550-600° C., the steam turbine has a single rotor shaft which contains high-pressure and low-pressure portions, and a temperature of the steam is not less than 530° C., wherein a thermal efficiency is not less than 46% and/or a specific power is not less than 600 kW/(kg/s). A temperature of the exhausted combustion gas at an inlet of the heat recovery steam generator is 550-600° C., a temperature of the exhausted combustion gas at an outlet of the heat recovery steam generator is not more than 130° C., a size of the blades for a last stage is not less than 30 inches at a blade portion thereof, a temperature of the steam at a high-pressure inlet of the steam turbine is not less than 530° C., and a temperature of the steam at a low-pressure outlet of the steam turbine is not more than 100° C.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a cross-sectional view of part of a gas turbine according to the present invention;

FIG. 2 is a perspective view of a blade for a compressor according to the present invention;

FIG. 3 is a graphical illustration of a heat treatment profile of the step cool method;

FIG. 4 is a cross-sectional view of an air inlet portion of the compressor according to the present invention;

FIG. 5 is a cross-sectional view of a cooling air inlet portion for a gas turbine having a two part compressor rotor constructed in accordance with the present invention;

FIG. 6 is a front view of a flange portion showing the air inlet portion of the compressor according to the present invention;

FIG. 7 is a cross-sectional view of a blade mounting portion of a rotor in the compressor according to the present invention;

FIG. 8 is a perspective view of a blade of the compressor used up to the fourth stage constructed in accordance with the present invention;

FIG. 9 is a schematic view of a uniaxial combined cycle power plant according to the present invention employing a gas turbine and a steam turbine;

FIG. 10 is a cross-sectional view of part of a reheating time high- and low-pressure steam turbine according to the present invention;

FIG. 11 is a table showing mechanical characteristics and heat-treatment conditions of rotor parts;

FIG. 12 is a table showing mechanical characteristics and heat-treatment conditions of rotor part f; and

FIG. 13 is a cross-sectional view of part of another gas turbine according to the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS EXAMPLE 1

Table 1 shows the chemical composition (weight percent) of the currently available disk materials and those of the combined rotor shafts according to the present invention. These samples were obtained by performing hot forging on the ingot melted by a high-frequency melting furnace. Comparative examples Nos. 1 and 2 are ASTM standard materials which are extensively used as the disk material. No. 1 is a Cr--Mo--V steel conforming to ASTM standard A470 Class 8, and No. 2 is a Ni--Cr--Mo--V steel conforming to ASTM standard A470 Class 7. Nos. 3 and 4 are Cr--Ni--Mo--V steels which are applied to the combined-type rotor shaft according to the present invention. Hardening and tempering corresponding to the central portion of the rotor, shown in Table 2, were conducted on these samples.

                  TABLE 1                                                          ______________________________________                                         Sample                                                                               Composition (wt. %)                                                      No.   C      Si      Mn   Ni   Cr    Mo   V    Others                          ______________________________________                                         1     0.27   0.25    0.72 0.42 1.15  1.20 0.23                                 2     0.25   0.03    0.04 3.65 1.74  0.40 0.12                                 3     0.23   0.03    0.20 1.85 2.05  1.38 0.25                                 4     0.23   0.03    0.18 1.80 2.00  1.35 0.25 Nb 0.02                         ______________________________________                                    

                  TABLE 2                                                          ______________________________________                                         Hardening    Tempering                                                         ______________________________________                                         No. 1 975° C. × 3 h                                                                Primary:    650° C. × 25 h                                                             Furnace                                                                        cooling                                        100° C./h                                                                          Secondary:  660° C. × 25 h                                                             Furnace                                        Cooling speed                   cooling                                  No. 2 850° C. × 3 h                                                                Primary:    590° C. × 25 h                                                             Furnace                                                                        cooling                                        100° C./h                                                                          Secondary:  605° C. × 25 h                                                             Furnace                                        Cooling speed                   cool ing                                 No. 3 940° C. × 3 h                                                                Primary:    590° C. × 25 h                                                             Furnace                                                                        cooling                                  No. 4 100° C./h                                                                          Secondary:  640° C. × 25 h                                                             Furnace                                        Cooling speed                   cooling                                  ______________________________________                                    

Table 3 shows the mechanical properties of the currently available rotor materials and the compressor combined rotor shaft materials. A room temperature tensile test, a V notch Charpy impact test and creep rupture test were conducted according to the JIS test methods. An impact test was conducted after step-cooling embrittlement, shown in FIG. 3, which was a simulation of high-temperature long-time embrittlement.

                                      TABLE 3                                      __________________________________________________________________________              0.2%                                                                      Tensile                                                                             Yield     Reduction                                                                           Impact  10.sup.5 hours Strength                        Sample                                                                             strength                                                                            point                                                                               Elongation                                                                          of area                                                                             value                                                                               Fatt                                                                              (kg/mm.sup.2)                                  No. (kg/mm.sup.2)                                                                       (kg/mm.sup.2)                                                                       (%)  (%)  kg-m/cm.sup.2                                                                       (° C.)                                                                     450° C.                                                                      475° C.                            __________________________________________________________________________     1   88.1 75.2 19.0 54.1  1.1 129                                                                               37   31.5                                      2   88.5 76.5 21.8 67.9 21.6 -38                                                                               31   25                                        3   89.1 76.8 20.2 70.0 15.4  5 42   35                                        4   88.2 76.0 21.3 71.2 17.5  -2                                                                               40.5 33.5                                      __________________________________________________________________________

The creep rupture strength was obtained by Larson-Miller method. The mechanical properties required for the compressor combined type rotor material are as follows: room temperature tensile strength ≧85 kg/mm², a fracture appearance transition temperature ≦20° C., and 538° C. 10⁵ h creep rupture strength ≧30 kg/mm². Although comparative example No. 1 satisfies the above-mentioned room temperature tensile strength and creep rupture strength, it has too high fracture appearance transition temperature and too low low-temperature toughness. Comparative example No. 2 satisfies the above-mentioned room temperature tensile strength and fracture appearance transition temperature but has too low creep rupture strength and too low high-temperature strength.

Samples 3 and 4 satisfy the above-mentioned room temperature tensile strength, fracture appearance transition temperature and creep rupture strength and are thus very useful as the compressor combined type rotor material.

As shown in FIG. 1, a gas turbine having a compressor according to the present invention includes a turbine tub shaft 10, a turbine bucket 3, a turbine stacking bolt 11, a turbine spacer 8, a distant piece 14, a nozzle 2, a compressor rotor shaft 6, a compressor blade 7, a compressor tub shaft 9a, a turbine disk 4. The gas turbine according to the present invention has compressor blades in seven of seventeen stages and turbine buckets three of three stages.

The gas turbine of this example is of heavy duty and single shaft type having a horizontally divided casing and a stacking rotor. The compressor is of seventeen stage axial flow type, and the turbine is of three stage impulse type. The stationary and moving blades are cooled by air in a single or two stages. The combustor is of berth flow type having sixteen chambers and employing the slot cool method.

The compressor rotor was manufactured from an alloy steel having a composition shown in Table 4.

                  TABLE 4                                                          ______________________________________                                                                    (wt. %)                                             C      Si         Mn     P       S    Ni                                       ______________________________________                                         0.24   0.02       0.20   0.004   0.003                                                                               1.78                                     ______________________________________                                         Cr        Mo     V          O.sub.2                                                                              Fe                                           ______________________________________                                         2.05      1.20   0.27       0.0015                                                                               Balance                                      ______________________________________                                    

Melting of the alloy steel was performed by a basic electric furnace. Refining was performed by a ladle. To obtain an ingot, both vacuum pouring and vacuum carbon deoxidation were performed. Next, casting was performed in a hot state (from 850° C. to 1200° C.) by a hydraulic press to obtain predetermined dimensions. The diameter of the rotor was 1300 mm, and the length thereof was 6000 mm. In the heat refining process, hardening was performed first by heating to 950° C. and then by water-spray quenching, and then tempering was conducted twice at 630° C. and 645° C. Table 5 shows the mechanical properties of the respective portions of the rotor. As shown in Table 5, the tensile strength of the respective portions was 88 kg/mm² or above and the impact absorbing energy thereof was 4.4 kg-m or above. The rotor was not embrittled. These valves prove that the rotor of this example has excellent properties.

Thus, the rotor shaft of this example can be used as the rotor for a gas turbine compressor.

The rotor shaft 6 of this example is a combined type rotor which extends from the stub shaft 9 to the distant piece 14. It has no central hole. The central hole may be formed in order to examine the mechanical properties.

                                      TABLE 5                                      __________________________________________________________________________                               Impact absorb-                                                                 ing energy                                                                             50/% Fatt                                                                              538° C., 10.sup.5 h                        0.2%     Reduc-                                                                             (kg-m)  (kg-m)  Creep                                        Tensile                                                                             Yield                                                                               Elon-                                                                              tion of                                                                            Before                                                                             After*                                                                             Before                                                                             After*                                                                             rupture                                      strength                                                                            point                                                                               gation                                                                             area                                                                               embrit-                                                                            embrit-                                                                            embrit-                                                                            embrit-                                                                            strength                                     (kg/mm.sup.2)                                                                       (kg/mm.sup.2)                                                                       (%) (%) ted ted ted ted (kg/mm.sup.2)                        __________________________________________________________________________     Low Outer                                                                              88.2 70.1 21  70  15.0                                                                               --  -40 --  --                                   pres-                                                                              layer                                                                      sure                                                                               portion                                                                    portion                                                                            Central                                                                            89.5 70.8 19  60  4.6 4.4   49                                                                               50  --                                       portion                                                                    High                                                                               Outer                                                                              88.3 70.1 21  70  16.2                                                                               --  -40 --  --                                   pres-                                                                              layer                                                                      sure                                                                               portion                                                                    portion                                                                            Center                                                                             88.7 70.3 20  64  4.5 4.4   55                                                                               55  17.2                                     portion                                                                    __________________________________________________________________________      *Heated at 500° C. for 3000                                       

Materials shown in Table 6, which are large steels having sizes corresponding to the actual sizes of various components for the gas turbine, were melted by the electro slug re-melting method, and then forged and heat treated. Forging was conducted in a temperature range from 850 to 1150° C. Heat treatment was conducted under the conditions shown in Table 6. Table 6 shows the chemical composition (weight percent) of each of the materials. Regarding the microscopic structure, sample Nos. 5 through 8 all have entire tempered martensitic structure, and sample No. 9 has an entire tempered bainite microstructure. Sample No. 5 was used to form the distant piece and the compressor disk of the last stage. The dimensions of the former were 60 mm (thickness)×500 mm (width)×1000 mm (length). The dimensions of the latter were 1000 mm (diameter) and 180 mm (thickness). Sample No. 6 was used to form a disk having dimensions of 1000 mm (diameter)×180 mm (thickness). Sample No. 7 was used to form a spacer having dimensions of 1000 mm (outer diameter)×400 mm (inner diameter)×100 mm (thickness). Sample No. 8 was used to form a turbine stacking bolt having dimensions of 40 mm (diameter)×500 mm (length) and a bolt which connects the distant piece to the turbine disk. Sample No. 9 was forged to form a turbine stub shaft having dimensions of 250 mm (diameter)×300 mm (length). Each of samples except for sample No. 8 was taken from the central portion of the material after being subjected to heat treatment in a direction perpendicular to an axial (longitudinal) direction thereof.

                                      TABLE 6                                      __________________________________________________________________________     Composition (%)                      Heat                                      No.   C  Si Mn Cr Ni Mo V  Nb N  Fe  treatment                                 __________________________________________________________________________     5     0.10                                                                              0.04                                                                              0.70                                                                              11.58                                                                             1.98                                                                              1.98                                                                              0.20                                                                              0.08                                                                              0.06                                                                              Balance                                                                            1050° C. × 5 hOQ             (Distant                              550° C. × 15 hAC            piece)                                600° C. × 15 hAC            6     0.10                                                                              0.05                                                                              0.65                                                                              11.49                                                                             1.70                                                                              2.04                                                                              0.19                                                                              0.08                                                                              0.06                                                                              "   1050° C. × 8 hOQ             (Turbine                              550° C. × 10 hAC            disk)                                 600° C. × 10 hAC            7     0.12                                                                              0.04                                                                              0.20                                                                              11.1                                                                              2.70                                                                              2.05                                                                              0.20                                                                              0.07                                                                              0.05                                                                              "   1050° C. × 3 hOQ             (Spacer)                              550° C. × 10 hAC                                                  600° C. × 10 hAC            8     0.10                                                                              0.03                                                                              0.69                                                                              11.94                                                                             1.86                                                                              2.25                                                                              0.21                                                                              0.15                                                                              0.05                                                                              "   1050° C. × 1 hOQ             (Stacking                             550° C. × 25 hAC            bolt)                                 600° C. × 2 hAC             9     0.26                                                                              0.25                                                                              0.79                                                                              1.09                                                                              0.41                                                                              1.25                                                                              0.23                                                                              -- -- "    975° C. × 8 hWQ             (CrMo steel)                          665° C. × 25 hAC                                                  665° C. × 25                __________________________________________________________________________                                          hAC                                        OQ: Oil quenching AC: Air cooling WQ: Water quenching                    

Table 7 shows the room temperature tensile strength, the 20° C. V notch Charpy impact value and the creep rupture strength of sample Nos. 5 through 9. The creep rupture strength was obtained by the normally used Larson-Miller method.

Sample Nos. 5 through 8 of the present invention (12% Cr steel) have a 450° C., 105 h creep rupture strength of 15 kg/mm2 or above and a 20° C. V notch Charpy impact value of 7 kg-m/cm² or above, and can thus satisfy the strengths required for the high-temperature gas turbine materials.

                                      TABLE 7                                      __________________________________________________________________________        Tensile                                                                             0.02%                                                                               Elon-                                                                              Reduction    10.sup.5 hours Creep                                strength                                                                            Yield                                                                               gation                                                                             of area                                                                             Impact value                                                                           rupture strengh                                  No.                                                                               (kg/mm.sup.2)                                                                       (kg/mm.sup.2)                                                                       (%) (%)  vE.sub.20 (kg-m/cm.sup.2)                                                              at 450° C. (kg/mm.sup.2)                  __________________________________________________________________________     5  112.0                                                                               79.3 19.8                                                                               60.1 8.7     51.1                                             6  111.7                                                                               79.5 20.1                                                                               59.3 8.3     52.3                                             7  114.3                                                                               81.2 19.5                                                                               62.5 7.2     51.3                                             8  115.7                                                                               82.6 22.3                                                                               63.4 8.7     52.7                                             9  86.4 -    26.7                                                                               68.8 7.5     35.2                                             __________________________________________________________________________

Although sample No. 9 (low alloy steel) for a stub shaft has a low 450° C. creep rupture strength, it has a tensile strength of 86 kg/mm² or above and a 20° C. V notch Charpy impact value of 7 kg-m/cm² or above, i.e., it has strengths required for a stub shaft (tensile strength ≧81 kg/mm² and 20° C. V notch Charpy impact value ≧5 kg-m/cm²).

The temperature of the distant piece and that of the compressor rotor shaft portion of the last stage, manufactured under the above-described conditions, are 450° C. at a maximum. The desirable thickness of the distant piece is between 25 and 30 mm. The turbine disk has a central through-hole. A compressive residual stress is applied to the through-hole of the turbine disk.

There are three stages of turbine disks 4. The turbine disks of the first and second stages located on the upstream side of the gas have a central hole. The alloys listed in Table 8 were used to form a turbine blade 3, a turbine nozzle 2, a liner 13 of a combustor 5, a compressor blade 7, a compressor nozzle 12, a diaphragm 15 and a shroud 1. Particularly, the turbine nozzle 2 and the turbine blade 3 were formed by casting.

A shroud segment (1) in Table 8 is used for the first stage located on the upstream side of the gas, and shroud segment (2) is used for both the second and third stages.

                                      TABLE 8                                      __________________________________________________________________________             C  Si Mn  Cr                                                                               Ni. Co  Fe  Mo B                                           __________________________________________________________________________     Turbine blade                                                                          0.15                                                                              0.10                                                                              0.12                                                                              15.00                                                                             Balance                                                                            9.02                                                                               --  3.15                                                                              0.015                                       Turbine nozzle                                                                         0.10                                                                              -- -- 20.2                                                                              Balance                                                                            21.5                                                                               --  -- 0.007                                               0.43                                                                              0.75                                                                              0.88                                                                              29.10                                                                             10.18                                                                              Balance                                                                            --  -- 0.010                                       Combustor liner                                                                        0.07                                                                              0.88                                                                              0.75                                                                              22.13                                                                             Balance                                                                            1.57                                                                               18.47                                                                              9.12                                                                              0.008                                       Compressor                                                                             0.11                                                                              0.41                                                                              0.61                                                                              12.07                                                                             0.31                                                                               --  Balance                                                                            -- --                                          Blade, nozzle                                                                  Shroud segment                                                                 (1)     0.08                                                                              0.87                                                                              0.75                                                                              22.16                                                                             Balance                                                                            1.89                                                                               18.93                                                                              9.61                                                                              0.005                                       (2)     0.41                                                                              0.65                                                                              1.00                                                                              23.55                                                                             25.63                                                                              --  Balance                                                                            -- --                                          Diaphragm                                                                              0.025                                                                             0.81                                                                              1.79                                                                              19.85                                                                             11.00                                                                              --  --  -- --                                          __________________________________________________________________________                W  Ti       Others                                                  __________________________________________________________________________     Turbine blade                                                                             3.55                                                                              4.12     Zr 0.15, Al 5.00                                        Turbine nozzle                                                                            7.55                                                                              2.32     Al 1.18, Ta 0.98, Nb 0.78                                          7.12                                                                              0.28     No 0.24, Zr 0.15                                        Combustor liner                                                                           0.78                                                                              --       --                                                      Compressor -- --       --                                                      Blade, nozzle                                                                  Shroud segment                                                                 (1)        0.85                                                                              --       --                                                      (2)        -- 0.25     Nb 0.33                                                 Diaphragm  -- --       --                                                      __________________________________________________________________________

A Y₂ O₃ stabilizing zirconia sprayed layer (or a CVD coating layer) is formed, as a heat-insulating layer, on the high temperature portion of the outer surface of each of the combustor liner 13, the moving blade 3 and the stationary blade 3 which are exposed to flames. In that case, an alloy layer whose composition comprises, in weight percent, of 2-5% Al, 20-30% Cr, 0.1-1% Y and the balance substantially of Ni or (Ni+Co) is formed between the base metal and the coated layer.

As shown in FIG. 2, with a combined rotor type compressor for a gas turbine, implantation or mounting of the blade is made possible when the length L of the hook of the blade has a relation expressed by L≦P/2 (where P is a pitch of the blades). The blade has a vane portion 16, a platform portion 17 and an implanted portion 18. The platform portion 17 has a protrusion 19 which protrudes toward the implanted portion 18.

In the case of a large compressor, since the blade located on the air inlet side is subjected to a high centrifugal force, it must be made of a material having a high specific strength. The blade located on the air outlet side is exposed to high temperatures, and thus must be made of a material having a high creep strength.

In this example, the blades from the first to fifth stages were made of Ti--6Al--4V alloy having a low specific gravity and a high tensile strength and shown in Table 9, while the blades from the sixth to seventeenth stages were made of 12Cr heat-resistant steel having a high high-temperature strength, and shown in Table 9.

                  TABLE 9                                                          ______________________________________                                         Sample                                                                               Composition (wt. %)                                                      No.   C      Si     Mn   Ni   Cr   Mo   V    Others                            ______________________________________                                         10    0.15   0.15   0.54 0.70 11.1 0.95 0.20 W 0.20,                                                                        Nb 0.15                                                                        N 0.04,                                                                        Fe Balance                        11    0.01   --     --   --   --   --   4.22 A 16.60                                                                        Fo 0.11,                                                                       Ti Balance                        ______________________________________                                    

The Ti--6Al--4V alloy blade was manufactured by performing annealing at 705° C. after hot forging. To obtain the 12Cr heat-resistant steel blade, oil hardening with heating to 110° C. and tempering at 650° C. were performed after melting and hot forging.

Table 10 shows the mechanical properties of the compressor blades.

A highly reliable compressor can be obtained by using the titanium alloy having a high specific strength for the blades to be located on the air inlet side while by using 12Cr heat-resistant steel having a high creep strength for the blades to be located on the air outlet side.

                  TABLE 10                                                         ______________________________________                                                      0.2%                                                                   Tensile Yield        Reduc-                                                                               Impact                                         Sam- strength                                                                               point  Elong-                                                                               tion  value 10.sup.5 hours Strength                  ple  (kg/    (kg/   ation of area                                                                              (kg-m/                                                                               (kg/mm.sup.2)                            No.  mm.sup.2)                                                                              mm.sup.2)                                                                             (%)   (%)   cm.sup.2)                                                                            450° C.                                                                        475° C.                    ______________________________________                                         10   103.7   87.0   19.6  65.9  6.2   48     43                                11   102.0   95.0   18.6  46.8  3.4   --     --                                ______________________________________                                    

In this example, the same number of ring-shaped grooves as the number of blade stages are formed in the circumferential surface of the rotor shaft 6. Each of the grooves has the substantially same cross-sectional shape as that of the implanted portion of the blade 7. Each of the grooves has a hole which allows the implanted portion to be inserted into the groove. The first blade which is first inserted into the respective groove through the hole and the last blade which is finally inserted therein are adjusted such that they do not come off from the groove through the hole. The adjacent blades are in contact with each other at the platform portions thereof to be fixed. A protrusion 19 of the blade is buried in the rotor shaft so that the platform portion is level with the surface of the rotor shaft.

Thus, it is possible to obtain a compression ratio of 15 through 18, a temperature from 400 to 500° C., a compression efficiency of 86% or above, a gas temperature at the turbine nozzle of the first stage of 360° C. or above, an exhaust temperature of 530° C. or above and a heat efficiency of 35% or above. Since the heat-resistant steel having a high creep rupture strength and showing less embrittlement is used to form the turbine disk, the distant piece, the spacer, the compressor rotor shaft and the stacking bolt, since the alloy having a high-temperature strength is used to form the turbine blade, since the alloy having high high-temperature strength and high-temperature ductility is used to form the turbine nozzle, since the alloy having high high-temperature strength and fatigue resistance is used to form the combustor nozzle, a highly reliably and well-balanced gas turbine can be obtained.

Most of the gas turbines have an inter cooler. In a gas turbine having no inter cooler, the temperature of the nozzle increases. The gas turbine according to the present invention is particularly suitably applied to such a non-inter cooler gas turbine. The turbine nozzles are formed for the first stage at 40 points over the entire periphery.

EXAMPLE 2

The reliability of the compressor combined type compressor rotor material is further enhanced by performing inclined heat treatment. That is, at an air inlet side used at a relatively low temperature, hardening is performed at a relatively low heating temperature (900° C.) to reduce the grain size of the material and thereby increase the low-temperature toughness. Conversely, at an air outlet side used at a relatively high temperature, hardening is performed at a relatively high heating temperature (950° C.) to increase the high-temperature strength of the material. In the tempering process performed after hardening, tempered bainite microstructure in which there was substantially no residual austenite was obtained substantially in whole of the combined type rotor. To obtain a high low-temperature toughness, tempering was repeated twice.

Table 11 shows the chemical composition of the combined rotor material which is subjected to the inclined heat treatment. Table 12 shows the conditions of the compressor inclined heat treatment. Table 13 shows the mechanical properties of the combined rotor material.

The inclined heat treatment greatly enhances the low-temperature toughness of the air inlet side portion and the high-temperature strength of the air outlet side. It is thus possible to obtain a more reliable combined type rotor.

                  TABLE 11                                                         ______________________________________                                         Composition (Weight %)                                                         No.  C       Si     Mn    Ni   Cr    Mo   V    Fe                              ______________________________________                                         12   0.23    0.03   0.18  1.78 2.01  1.45 0.26 Balance                         ______________________________________                                    

                  TABLE 12                                                         ______________________________________                                                Hardening Tempering                                                     ______________________________________                                         Air inlet                                                                               900° C. Water                                                                       Primary:   590° C. Furnace                         side (low                                                                               spray cooling          cooling                                        portion) corresponding                                                                  to 100° C./h                                                                        Secondary: 635° C. Furnace                                  cooling speed          cooling                                        Air outlet                                                                              950° C. Water                                                                       Primary:   590° C. Furnace                         side (high-                                                                             spray cooling          cooling                                        temperature                                                                             corresponding                                                         portion) to 100° C./h                                                                        Secondary: 650° C. Furnace                                  cooling speed          cooling                                        ______________________________________                                    

                                      TABLE 13                                     __________________________________________________________________________                0.2%                   10.sup.5 hours                               Tensile    Yield     Reduction                                                                           Impact  Strength                                     strength   point                                                                               Elongation                                                                          of area                                                                             value                                                                               Fatt                                                                              (kg/mm.sup.2)                                (kg/mm.sup.2)                                                                             (kg/mm.sup.2)                                                                       (%)  (%)  kg-m/cm.sup.2                                                                       (° C.)                                                                     450° C.                                                                     475° C.                           __________________________________________________________________________     Air inlet                                                                            91.2 79.1 21.3 70.5 22.5 -20                                                                               --  --                                       side (low                                                                      temperature                                                                    portion)                                                                       Air outlet                                                                           91.8 80.0 20-.3                                                                               67.9 6.3     8                                                                              43.0                                                                               36.5                                     side (high-                                                                    temperature                                                                    portion)                                                                       __________________________________________________________________________

EXAMPLE 3

The combined-type rotor was obtained by the electro slug re-melting method (hereinafter abbreviated as ESR method) using two types of electrodes.

A material having a high low-temperature toughness was used to form an air inlet side portion of the rotor, and a material having a high high-temperature strength was used to form an air outlet side portion thereof. First, a material of sample No. 14 was melted as the air outlet side portion, and then a material of sample No. 13 was melted as the air inlet side portion to be combined with the air outlet side portion. This combined ingot was hot forged and then inclination heat treated.

Table 14 shows the chemical composition (weight percent) of the combined rotor material for a compressor obtained by ESR. Table 15 shows the conditions of the heat treatment. Table 16 shows the mechanical properties of the combined rotor material for a compressor obtained by ESR.

The combined rotor material for a compressor obtained by ESR has a very high low-temperature toughness for the air inlet side portion and a very high high-temperature strength for the air outlet side portion, and is thus highly reliable.

                  TABLE 14                                                         ______________________________________                                         Sample                                                                               Composition (wt. %)                                                      No.   C      Si      Mn   Ni   Cr    Mo   V    Fe                              ______________________________________                                         13    0.25   0.03    0.05 3.71 1.75  0.38 0.12 Balance                         14    0.23   0.02    0.19 1.75 1.51  1.60 0.25 Balance                         ______________________________________                                    

                  TABLE 15                                                         ______________________________________                                                    Heat treatment condition                                            No.              Hardening Tempering                                           ______________________________________                                         14   Air inlet side                                                                             850° C.                                                                           Primary:                                                                               590° C. Furnace                           (low-temperature                                                                           Water spray       cooling                                          portion)    cooling   Secondary:                                                                             605° C. Furnace                                                         cooling                                     15   Air outlet side                                                                            940° C.                                                                           Primary:                                                                               590° C. Furnace                           (High-temper-                                                                              Water spray       cooling                                          ature       cooling   Secondary:                                                                             640° C. Furnace                           portion)                      cooling                                     ______________________________________                                    

                                      TABLE 16                                     __________________________________________________________________________                0.2%                   10.sup.5 hours                               Tensile    Yield     Reduction                                                                           Impact  Strength                                     strength   point                                                                               Elongation                                                                          of area                                                                             value                                                                               Fatt                                                                              (kg/mm.sup.2)                                (kg/mm.sup.2)                                                                             (kg/mm.sup.2)                                                                       (%)  (%)  kg-m/cm.sup.2                                                                       (° C.)                                                                     450° C.                                                                     475° C.                           __________________________________________________________________________     Air inlet                                                                            88.5 74.2 21.5 86.8 21.5 -35                                                                               -- --                                        side (low                                                                      temperature                                                                    portion)                                                                       Air outlet                                                                           87.1 73.8 20.6 69.9 8.8    26                                                                              43.5                                                                              37.5                                      side (high-                                                                    temperature                                                                    portion)                                                                       __________________________________________________________________________

EXAMPLE 3

FIG. 4 is a cross-sectional view illustrating the cooling air introducing method for a gas turbine driven by a compressor with a combined type rotor according to the present invention.

The turbine disk can be cooled by providing a cooling air introducing hole in the flange portion of the shaft. Machining of the cooling air introducing hole in the flange portion is very easy and enables the number of hours required for manufacture to be greatly reduced.

EXAMPLE 4

A high-temperature large-size gas turbine compressor of this example has a two-part type rotor. In that case, the cooling air introducing hole is formed in the flange portion of the divided rotor.

The compressor rotor of FIGS. 5 and 6 is divided into two parts between the blade of the last stage (seventeenth stage) and the blade of the previous stage (sixteenth stage). The two parts are constructed so as to be combined with each other by bolts. The divided position is at the cooling air inlet port, preferably, at one of the compressor's stages whose pressure is higher than that of the cooling air outlet of the turbine.

As shown in Table 17, a material of Sample No. 15, which is 3.5 Ni--Cr--Mo--V steel having a high low-temperature toughness, was used for the part of rotor of the air inlet side, and a material of Sample No. 16, which is 1.8 Ni--Cr--Mo--V steel having a high high-temperature strength, was used for the another part of rotor of the air outlet side. Table 18 shows the heat treatment conditions. Table 19 shows the mechanical properties of the two-part rotor materials for a compressor.

According to this example, reliability can be enhanced and the number of man-hours for manufacture can be reduced when compared with the conventional divided type compressor.

                  TABLE 17                                                         ______________________________________                                         Composition (wt. %)                                                            No.  C       Si     Mn    Ni   Cr    Mo   V    Fe                              ______________________________________                                         15   0.25    0.04   0.04  3.75 1.70  0.40 0.13 Balance                         16   0.23    0.03   0.20  1.75 1.50  1.60 0.25 Balance                         ______________________________________                                    

                  TABLE 18                                                         ______________________________________                                                    Heat treatment condition                                                             Quenching                                                     No.              (Hardening)                                                                              Tempering                                           ______________________________________                                         15   Air inlet side                                                                             850° C.                                                                           Primary:                                                                               590° C. Furnace                           (low-temperature                                                                           Water spray       cooling                                          portion)    cooling   Secondary:                                                                             605° C. Furnace                                                         cooling                                     16   Air outlet side                                                                            940° C.                                                                           Primary:                                                                               590° C. Furnace                           (High-temper-                                                                              Water spray       cooling                                          ature portion)                                                                             cooling   Secondary:                                                                             640° C. Furnace                                                         cooling                                     ______________________________________                                    

                                      TABLE 19                                     __________________________________________________________________________                0.2%                   10.sup.5 hours                               Tensile    Yield     Reduction                                                                           Impact  Strength                                     strength   point                                                                               Elongation                                                                          of area                                                                             value                                                                               Fatt                                                                              (kg/mm.sup.2)                                (kg/mm.sup.2)                                                                             (kg/mm.sup.2)                                                                       (%)  (%)  kg-m/cm.sup.2                                                                       (° C.)                                                                     450° C.                                                                     475° C.                           __________________________________________________________________________     Air inlet                                                                            89.1 74.8 21.7 70.8 23.2 -47                                                                               --  --                                       side (low                                                                      temperature                                                                    portion)                                                                       Air outlet                                                                           88.2 73.9 20.9 70.2 11.8   15                                                                              43.3                                                                               37.2                                     side (high-                                                                    temperature                                                                    portion)                                                                       __________________________________________________________________________

EXAMPLE 5

As shown in FIG. 7, the blades from the first stage to the fourth stage are implanted or mounted in the same manner as that of the disk type rotor, while a cavity portion 20 is formed in the implanted portion of the rotor shaft from the twelfth stage to the last stage, unlike example 1.

In FIG. 8 the blade used up to the fourth stage is depicated, with the implanted portion of the implanted blade being fixed by a spacer at both sides thereof.

The cavity portions 20 (FIG. 7) are provided to suppress an increase in temperature of the rotor shaft due to the compressed air heated to a high temperature at the last stage side, and thereby reduce the temperature gradient due to a rapid increase in temperature of the rotor shaft.

It has been confirmed that the gas turbine of this example has excellent heat efficiency and facilitates maintenance.

EXAMPLE 6

As shown in FIG. 9, the power plant of the present invention can employ a plurality of such gas turbines and a plurality of such steam turbines. For example, three gas turbines and three steam turbines or six gas turbines and six gas steam turbines may be employed.

In recent years, there is a tendency toward the use of a combined cycle power plant in which a generator is driven by both a gas turbine driven using liquefied natural gas (LNG) as a fuel and a steam turbine driven by the steam obtained by recovering the exhaust gas energy of the gas turbine. The use of such a combined cycle power plant can increase heat efficiency to 46% or above from 40% of heat efficiency obtained in a conventional power plant which employs a steam turbine alone.

As mentioned above, such a combined cycle power plant is generally of single fuel combustion type which employs liquefied natural gas (LNG). However, attempts have been made in recent years to use both liquefied natural gas (LNG) and liquefied petroleum gas (LPG) in such a power plant, or to provide a fuel mixing combustion type power plant which employs both LNG and LPC to smooth the plant operation and to enhance economy.

First, air is taken into an air compressor of a gas turbine through a suction filter and then a suction silencer. The air compressor compresses the air and sends the compressed air to a low NOx combustor.

In the combustor, a fuel is injected into this compressed air and fired to generate a high-temperature gas having a temperature of 1400° C. or above. This generated high-temperature gas does work in the gas turbine to generate power.

The exhaust gas having a temperature of 550° C. or above and discharged from the gas turbine is supplied to an exhaust heat energy recovery steam generator (boiler) through an exhaust gas muffler device. The heat recovery steam generator recovers heat energy in the gas and sends a high pressure steam and a low pressure steam having a temperature of 530° C. or above to a steam turbine through a low-pressure steam pipe and a high-pressure steam pipe, respectively. The heat recovery steam generator includes a denitrating device of the type which employs the dry ammonia catalytic reduction method. The exhaust gas is discharged to the atmosphere from a tripod aggregation type chimney having a height of several hundreds of meters.

The generated high- and low-pressure steams are supplied to a steam turbine which includes a high-pressure rotor portion and low-pressure rotor portion of the combined type rotor. The steam turbine will be described in detail hereinbelow.

The steam discharged from the steam turbine flows into a condenser. The water condensate generated by vacuum deaeration in the condenser passes through a condensate pump which increases the pressure of the condensate. The feed water from the condensate pump is sent to the heat recovery steam generator again. The generator is driven by both the gas turbine and the steam turbine at the respective shaft ends thereof to generate power. In order to cool the blades of the gas turbine used in such a combined cycle power plant, the steam utilized by the steam turbine may be used as a cooling medium, or alternatively air is generally used as the cooling medium. Since the steam has a much higher specific heat than air and is light in weight, the use of steam is thus advantageous in cooling efficiency. Since the steam has the high specific heat, when it is discharged into a main stream of gas after cooling the turbine blade, a temperature of the main gas stream greatly reduces, thus reducing the efficiency of the entire plant. Hence, the steam in the steam turbine having a relatively low temperature (about 800° C.) is supplied though a cooling medium supply port of the gas turbine blade to cool a blade body, and the cooling medium heated to a relatively high temperature (about 900° C.) as a consequence of heat exchange is returned to the steam turbine. In this manner, a reduction in temperature of the main stream of gas (which is between 1300° C. and 1550° C.) is prevented, and the efficiency of the steam turbine is improved, thus improving the efficiency of the entire plant. Such a combined cycle power plant can generate 90,000 KW of power in which about 60,000 KW is generated by the gas turbine and 30,000 KW is generated by the steam turbine. The steam turbine of this example is compact, and can thus be manufactured economically as compared with a large steam turbine having the same capacity. This allows for an economical operation of the plant when the generated power varies.

Any of the gas turbines described above can be employed. The air compressed by the compressor is supplied to the combustor to generate a combustion gas having a temperature of 1400° C. or above. The generated combustion gas rotates the disks with the blades implanted therein.

With the construction of FIG. 10, the output of the single turbine can be increased by increasing the pressure and temperature of the steam at the main steam inlet of that high- and low-pressure steam turbine to 100 atg or above and 530° C. or above, respectively. To achieve an increase of the output of the single turbine, the length of the blade of the last stage and the steam flow rate must also be increased. An increase in the length of the blade of the last stage from, for example, 26 inches to 33.5 inches increases the annular area defined by the distal ends of the blades as viewed in the longitudinal direction of the steam turbine by a factor of 1.7, increasing the output of the single turbine from conventional 100 MW to 1700 MW. An increase in the length of the blade to 40 inches increases the output of the single turbine by a factor of 2.

In a steam turbine whose blade has a length of 33.5 inches or above, the high- and low-pressure rotor may be made of a Cr--Mo--V steel containing 0.5% Ni. Such a rotor material has been developed originally for a high-temperature portion. Thus, it has excellent high-temperature strength and creep characteristics, and can be used even when the pressure and temperature of the steam at the main steam inlet portion increases. In the case of a blade having a length of 26 inches, the tangential stress generated in a rated rotating state at the low-temperature portion, particularly, in the central hole of the turbine rotor portion corresponding to the blade of the last stage, is about 0.95 in terms of the stress ratio (acting stress/allowable stress). In the case of a blade having a length of 33.5 inches, about 1.1 is obtained as the stress ratio. These valves indicate that the rotor material cannot be used for the low-temperature portion.

3.5% Ni--Cr--Mo--V steel may also be used as the rotor material. Since this rotor material has a toughness in the low-temperature area and hence has a tensile strength and proof stress higher than those of Cr--Mo--V steel by 14% in the low-temperature area, even when a blade having a length of 33.5 inches is used, the obtained stress ratio is about 0.96. In the case of a blade having a length of 40 inches, the stress ratio increases to 1.07, which means that the rotor material cannot be used for a low-temperature area. 3.5% Ni--Cr--Mo--V steel has a creep rupture stress which is about 0.3 times that of Cr--Mo--V steel, and thus cannot be used for the high-temperature area because of an insufficient high-temperature strength.

Hence, in order to achieve a high output, a rotor mate rial which satisfies the excellent characteristics of Cr--Mo--V steel for a high-temperature area and excellent characteristics of Ni--Cr--Mo--V steel for a low-temperature area is required.

When a blade having a length of thirty inches or above, i.e., in the order of forty inches, is used, since the stress ratio is 1.07, as stated above, a material having a tensile strength of 88 kg/mm² or above is required. For a high- and low-pressure steam turbine rotor in which a blade of thirty-three inches or above is mounted, a material having a 538° C., 10⁵ h creep rupture strength of 15 kg /mm² or above is required from the viewpoint of prevention of high-temperature rupture at a high-pressure side. From the viewpoint of prevention of derusting at a low-pressure side, a material having a room temperature impact absorbing energy of 2.5 kg-m (3 kg-m/cm²) is required.

In the steam turbine of this example, blades 24 of fifteen stages are implanted in a high-pressure rotor portion and low-pressure rotor portion of the combined rotor shaft 23. Steam which passes through a steam control valve 25 flows into a high-pressure portion 30 from a steam inlet 34 as a high-temperature, high-pressure steam of 538° C. and 126 atg. The steam which flows out from the high-pressure portion 30 is a steam of 367° C. and 38 atg. This steam is re-heated to 538° C. and 35 atg by a re-heater 33 of the heat recovery steam generator. The re-heated steam passes through a low-pressure portion 31 of the rotor, and is discharged from an outlet 22 into the condenser as a steam of about 46° C. and 0.1 atg. Reference numeral 32 denotes a bearing.

Since the high-pressure rotor portion and low-pressure rotor portion combined rotor shaft 23 of this example is exposed to steam having a temperature ranging from 538° C. to 46° C., a forged steel of a Ni--Cr--Mo--V low alloy, exhibiting FATT 60° C. or below, 538° C., 10⁵ h strength of 11 kg/mm² or above, is used to form the rotor shaft. The implanting portion of the rotor shaft 23 into which the blade 24 is implanted has a disk-like shape, and is manufactured by cutting the rotor shaft 23. As the length of the blade reduces, the length of the disk portion is reduced in order to lessen vibrations.

As the material of the rotor shaft 23 of this invention, an ingot was manufactured from an alloy steel having a composition shown in Table 4 by the electro slug re-melting method. The obtained ingot was hot forged to a diameter of 1.2 m. After the ingot was heated at 950° C. for 10 hours, it was rotated and water spray cooled such that the central portion of the rotor shaft is cooled by a cooling speed 100° C./h. Next, tempering was conducted by retaining the shaft at 665° C. for 40 hours. A sample was cut out from the central portion of this rotor shaft. A creep rupture test, a V notch impact test before and after heating (heating at 500° C. for 3000 hours) (the cross-sectional area of the sample was 0.8 cm²) and the tensile test were conducted on the sample.

(1) High-pressure rotor portion and low-pressure rotor portion combined rotor shaft

In this example, a Ni--Cr--Mo--V low alloy steel having the substantially same composition and structure as those of the compressor rotor shaft material can be used as this turbine rotor shaft material. More preferably, this steel may have a (Mn/Ni) weight percent ratio of 0.12 or a below, or (Si+Mn)/Ni weight percent ratio of 0.18 or below. This steel may have a (V+Mo)/(Ni+Cr) weight percent ratio ranging from 0.45 to 0.70. At least one of 0.04% (weight percent) or less rare earth element, 0.04% or less Mg, 0.04% or less Ca, 0.2% or less Hf, 0.2% or less Zr and 1% or less W may be added to that low alloy steel.

(2) Blade

Each of the blades for three stages on the high-temperature, high-pressure side has a length of about 40 mm, and is made of a martensitic forged steel whose composition comprises, in weight percent, 0.20-0.30% C, 10-13% Cr, 0.5-1.5% Mo, 0.5-1.5% W, 0.1-0.3% V, 0.5% or less Si, 1% or less Mn and the balance substantially of Fe.

The blades for the intermediate pressure portion, the lengths of which gradually increase toward the low pressure side, are made of a martensitic forged steel whose composition comprises, in weight percent, 0.05-0.15% C, 1% or less Mn, 0.5% or less Si, 10-13% Cr, 0.5% or less Mo, 0.5% or less Ni and the balance substantially of Fe.

The blade of the last stage has a length of 33.5 inches, and is made of a martensitic forged steel whose composition comprises, in weight percent, 0.08-0.15% C, 1% or less Mn, 0.5% or less Si, 10-13% Cr, 1.5-3.5% Ni, 1-2% Mo, 0.2-0.5% V, 0.02-0.08% N and the balance substantially of Fe. There are about ninety blades over the periphery. On this last stage, an errosion-preventing shielding plate which is a stellite plate is provided at the leading edge of the distal end thereof by welding. Besides the provision of the shielding plate, tempering is conducted partially on the last stage. As a blade having a length of 40 inches or above, a Ti blade containing 5-8% Al and 3-6% V is used.

On each stage, four to five blades are fixed by a shroud plate made of the same material as that of the blades by caulking a protruding tenon provided at the distal end thereof.

To achieve 3000 rpm, 12% Cr steel is used for a blade having a length of 40 inches. For 3600 rpm, a Ti blade is used as a blade having a length of 40 inches. A blade having a length up to 33.5 inches is made of 12% Cr steel.

(3) Stationary blades 27 of three stages on the high-pressure side are made of a martensitic steel having substantially the same composition as that of the moving blades. The stationary blades 27 of the other stages are made of substantially the same material as that of the moving blades on the intermediate pressure portion.

(4) A casing 26 is made of a Cr--Mo--V cast steel whose composition comprises, in weight percent, 0.15-0.3% C, 0.5% or less Si, 1% or less Mn, 1-2% Cr, 0.5-1.5% Mo, 0.05-0.2% V, 0.1% or less Ti. Reference numeral 28 denotes a generator which can generate power of 100,000 to 200,000 KW. The length between the bearings 32 of the rotor shaft is about 520 cm. The outer diameter at the last stage blades is 316 cm. A rate of this outer diameter to the length between the bearings is 1.65. The plant capacity is 100,000 KW. The length between the bearings per 10,000 KW of plant capacity is 0.52 m.

In this example, the outer diameter, when the last stage blade having a length of forth inches is used, is 365 cm. The rate of the length between the bearings to this outer diameter is 1.43. With this arrangement, a plant capacity of 200,000 KW is obtained. The distance between the bearings per 10,000 KW is 0.26.

A rate of the outer diameter of the blade implanting portion of the rotor shaft to the length of the last stage blade is 1.70 in the case of a blade of 33.5", and is 1.71 in the case of a blade of 40".

In this example, the steam temperature may also be 566° C., and the steam pressure may be either 121, 169 or 224 atg.

The plant of this example is of uniaxial type which includes six pairs of power plants each power plant including a gas turbine, a heat recovery steam generator, a steam turbine and a generator. However, the plant may also be of multi-shaft type in which a single steam turbine is driven using a steam obtained by combinations of a plurality of gas turbines and corresponding heat recovery steam generators.

In a uniaxial type power plant, the gas turbine generates 2/3 of the entire plant output with the remaining 1/3 generated by the steam turbine. A gas turbine which generates 50,000 KW to 200,000 KW of power can also be employed. In that case, a steam turbine corresponding to that output of the gas turbine is used.

The heat efficiency of the power plant can be increased by 2 to 3% from that of a conventional thermal power plant. Further, since the plant can be operated near the rated load which assures a high heat efficiency by reducing the number of gas turbines to be operated, the heat efficiency of the entire plant can be maintained to 46% or above. In addition, since the amount of CO₂ generated per unit plant capacity can be reduced, the plant can contribute to minimization of the earth warming trend.

The combined cycle power plant requires a short time to stop the operation thereof, and is made up of combinations of easy gas turbines and small and simple steam turbines. Therefore, the plant capacity of the power plant can be readily adjusted. This makes the power plant suitable as a middle load thermal power plant.

Since development of the technology has greatly increased reliability of the gas turbine and since the combined cycle power plant is made of up combinations of small-capacity machines, even if a failure occurs, it may affect only part of the plant, making the combined cycle power plant a reliable power source.

As will be understood from the foregoing description, in the present invention, loosening of the bolts due to creep thereof can be substantially eliminated as compared with a conventional divided type disk. Consequently, air having higher temperatures and higher pressure can be supplied to a combustor or a turbine to cool the same, enabling the temperature of the combustion gas to be increased to 1400° C. or above while making efficient cooling possible. As a result, the heat efficiency of the gas turbine can be increased, and a combined cycle power plant having a higher efficiency can be obtained.

EXAMPLE 7

Each of the above described alloys as shown in Table 1 and prepared as described before can be used as materials for a divided-type rotor according to the present invention. The alloys are prepared in the high-frequency induction melting furnace, and are changed to divided-type rotor part samples through a forging process. The samples are heat-treated as Table 2, and mechanical characteristics thereof after the heat treatment are shown in Table 3.

In comparison with the mechanical characteristics required for divided-type rotor parts used at the highest temperature area (room temperature tensile strength 85≧Kg/mm², fracture appearance transition temperature (Fatt) ≦20° C., 538° C. 10⁵ hours creep rupture strength ≧30 Kg/mm²), Fatt of the Sample No. 1 is high for low temperature toughness, but the room temperature tensile strength and creep rupture strength thereof are enough for a divided-type rotor part e used in a relatively high-temperature. The creep rupture strength of the Sample No. 2 is low for high temperature strength, but the room temperature tensile strength and Fatt are enough for divided-type rotor parts a-d used in a relatively low-temperature at the gas-flow upstream side. The room temperature tensile strength, Fatt and creep rupture strength of the Samples No. 3 and 4 are enough also for divided-type rotor parts e and f used in the relatively high-temperature, particularly for the divided-type rotor part f. All of the divided-type rotor parts a-f can be made of the Samples No. 3 and 4. Therefore, as shown in FIG. 13, the compressor rotor can be formed by a combination of the rotor parts a-f made of a common material.

The blades 16 of the first and second stages are implanted in the rotor part a, the blades 16 of the third and fourth stages are implanted in the rotor part b, the blades 16 of the fifth and sixth stages are implanted in the rotor part c, the blades 16 of the seventh and eighth stages are implanted in the rotor part d, the blades 16 of the ninth to eleventh stages are implanted in the rotor part e, and the blades 16 of the twelfth to seventeenth stages are implanted in the rotor part f, and the rotor parts a-f are combined fixedly with each other by bolts 19 extending between the blades 16 of the second stage and the last stage. The rotor part f and the distant piece 14 are combined with each other by at least ten bolts made of a heat resistant steel. Since the rotor parts a-e are used at not more than 350° C., the high temperature strength (creep rupture strength) thereof is not required, but the low temperature toughness thereof should be high. Particularly, since the rotor part a has a slide bearing portion and long vanes implanted therein, the lowest temperature (35° C.) and a large centrifugal force are applied to the rotor part a. Therefore, the rotor part a must have the highest low-temperature-toughness in comparison with the other rotor parts. On the other hand, since the highest temperature (≦400° C.) is applied to the rotor part f, the creep rupture strength and oxidation-resistant characteristic of the rotor part f should be high.

Each of the rotor parts a-d has grooves inclined relative to the axial direction of the rotor so that the blades 16 (as shown in FIG. 2) for two stages are received therein. In each of the rotor parts e and f, the blades 16 for three stages are implanted, the blades 16 (as shown in FIG. 8) are implanted at both axial sides of rotor part, and a circumferential groove at an axial center of rotor part receives the blades 16 shown in FIG. 2. In the distant piece 12 at a downstream side of the rotor part f, the blades 16 for three stages are implanted, the blades 16 (as shown in FIG. 8) are implanted at both axial sides of rotor part as in the rotor parts a-d, and the circumferential groove at the axial center of distant piece receives the blades 16 shown in FIG. 2. Diameters of the rotor parts a-c are substantially equal to each other, the diameters of the rotor parts d and e increase gradually, and the rotor part f has the maximum diameter in comparison with the other rotor parts a-e. A ratio of an axial distance over the blades 16 of all stages to the maximum diameter of the rotor parts a-f is 3.4-3.8 to 1, and another ratio of the axial distance over the blades 16 of all stages to the minimum diameter of the rotor parts a-f is 4.0-4.4 to 1. The rotor parts a-f have respective cylindrical shapes to form an axial hollow therein so that a weight of the rotor parts a-f is decreased.

A radial length of the blades 16 implanted in the rotor part f and that of blades 16 implanted in the distance piece 14' are substantially equal to each other. Radial lengths of the blades 16 implanted in the rotor parts a-e decrease gradually from the gas flow upstream side toward the gas flow downstream side. A ratio of the radial length of the blades 16 of the last stage to that of the first stage is 3.45 to 1, preferably, 4-5 to 1. The rotor parts b-f are disk-shaped, and the rotor parts d-f have respective ring-shaped spaces at radially inner sides of the implanted blades 16. Axial distances between the blades 16 adjacent axially to each other decrease gradually from the first stage to the eighth stage, those of the eighth to tenth stages are substantially equal to each other, and those of the eleventh to seventeenth stages are substantially equal to each other and are smaller than those of the eighth to tenth stages. A ratio of the axial distance of the blades between the first stage and the second stage to that between the sixteenth stage and the seventeenth (last) stage is 2.7-3.2 to 1, and a ratio of the radial length of the blades 16 of the first stage to that of the seventeenth stage is 3.5-4.2 to 1. The nozzle for compressor is made of SUS 410 or SUS 410J1.

In these embodiments, the blades 16 (as shown in FIG. 8) are implanted in the grooves 21 (as shown in FIG. 7) inclined relative to the axial direction, or the blades 16 (as shown in FIG. 2) are implanted in the ring-shaped circumferential grooves 21 with insert holes through which the implanted portions of the blades 16 are inserted into the ring-shaped grooves 21. The blades 16 are positioned so as to arrange each of the insert holes between the blades 16. Platforms of the blades 16 adjacent to each other in each of the grooves contact each other. The projections 19 of the blades 16 are implanted in the rotor, and the platforms of the blades 16 and outer surface of the rotor form a flat periphery of rotor.

EXAMPLE 8

The rotor parts a-f and diststant piece 14' of the divided type rotor may be made of the ESR alloys (obtained by the electro slug re-melting method using two types of electrodes) as shown in Tables 14-16. The ESR alloys are heat-treated after hot forging. The rotor parts a-c of the gas flow upstream side are made of the ESR alloy with high low-temperature toughness (tensile strength ≧80 Kg/mm², V-notch impact value ≧15 kg-m/cm², Fatt ≦0° C.), and the parts d-f and distant piece 14' of the gas flow downstream side are made of the ESR alloy with high high-temperature strength (tensile strength ≧80 Kg/mm², 450° C. 10⁵ hours creep rupture strength ≧35 Kg/mm², preferably 40 Kg/mm²).

EXAMPLE 9

The compressor with the divided type rotor as described above may be used in the uniaxial combined type power plant. In this case, the blades 16 of the fifteenth to seventeenth (last three) stages of the compressor rotor are made of the before-mentioned martensitic forged steel whose composition comprises, in weight percent, 0.20-0.30% C, 10-13% Cr, 0.5-1.5% Mo, 0.5-1.5% W, 0.1-0.3% V, 0.5 or less % Si, 1 or less % Mn and the balance substantially of Fe. The blades 16 of the first stage of the compressor rotor are made of the before-mentioned martensitic steel or Ti alloy, as the blades of the last stage of the steam turbine. The nozzle of the compressor is made of ferritic stainless steel including 13 weight percent Cr.

EXAMPLE 10

The rotor parts a-f of the divided type rotor as described above may be made of the alloy shown in Table 4. The melting of the alloy is performed by the basic electric furnace, and refined by the ladle. The vacuum pouring and vacuum carbon deoxidation are performed to form the ingot. The hot forging is performed by the hydraulic press machine to divide the ingot into six parts thereof for the rotor parts and to obtain predetermined respective dimensions for the rotor parts. FIG. 12 shows mechanical characteristics of center portions of the rotor parts a, c and f made of the above alloy and heat-treatment conditions therefor. The heat treatments for the rotor parts b, d and e are substantially similar to those for the rotor part a or c. As shown in FIG. 13, even after brittling, the rotor part f keeps the room temperature tensile strength ≧85 Kg/mm² and the impact absorbing energy in 20° C.≧23 kg-m/cm². Therefore, the alloy can be used for all of the rotor parts. 

What is claimed is:
 1. A high-temperature gas turbine including a compressor for compressing an air, and a turbine coupled to the compressor and rotated by a combustion gas, whereinthe compressor has a rotor including a plurality of rotor parts, and blades for a plurality of stages implanted in the rotor parts, the rotor part in which the blades for the last stage are implanted is made of a Ni--Cr--Mo--V low alloy steel, and the Ni--Cr--Mo--V low alloy steel has substantially an entire bainite microstructure comprising, in weight percent, C of 0.15-0.40%, Si not more than 0.1%, Mn not more than 0.5%, Ni of 1.5-2.5%, Cr of 0.8-2.5%, Mo of 0.8-2.0%, V of 0.1-0.35% and the balance being substantially Fe.
 2. A high-temperature gas turbine according to claim 1, wherein the Ni--Cr--Mo--V low alloy steel further comprises, in weight percent, at least one of Nb and Ta of 0.01-0.1%.
 3. A high-temperature gas turbine including a compressor for compressing an air, and a turbine coupled to the compressor and rotated by a combustion gas, whereinthe compressor has a rotor including at least three rotor parts, and blades for at least fifteen stages implanted in the rotor parts, the blades for the first stage and at least one stage of the second to fifth stages are made of a Ti alloy, and the blades for the second to the last stages other than the blades made of the Ti alloy are made of a martensite stainless steel.
 4. A high-temperature gas turbine including a compressor for compressing an air, and a turbine coupled to the compressor and rotated by a combustion gas, whereinthe compressor has a rotor including a plurality of rotor parts, and blades for a plurality of stages implanted in the rotor parts, each of the rotor parts in which the blades are implanted is made of a Ni--Cr--Mo--V low alloy steel, and the Ni--Cr--Mo--V low alloy steel has substantially an entire bainite microstructure comprising, in weight percent, C of 0.15-0.40%, Si not more than 0.1%, Mn not more than 0.5%, Ni of 1.5-2.5%, Cr of 0.8-2.5%, Mo of 0.8-2.0%, V of 0.1-0.35% and the balance being substantially Fe. 